Cadmium Octoate reduces rapid film formation and therefore improves through drying. It prevents wrinkling and is used in combination with primary and auxiliary driers. VISCOSITY (AT 30°C) SEC. Worldwide Exports

Barium is a soft, silvery metal that rapidly tarnishes in air and reacts with water. Barium is not an extensively used element. Most is used in drilling fluids for oil and gas wells. It is also used in paint and in glassmaking. Worldwide Exports

ARIOXIME Methyl Ethyl Ketoxime (MEKO) is clear liquid, which is used in a variety of application. It is used for its properties as an oxidant, metal complexing agent, and versatile blocking group and it prevents skinning in alkyd-based systems. Worldwide Exports

Test Particulars Observed Value Remarks Viscosityat30°CBrookfield Viscometer, Cps SPINDLE NO. 5 50RPM 5200 OK THIXOTROPIC INDEX 5/50 4.5 OK GelTime,minutesat30°C 1.0%v/wCobaltOctoate (3%Co) 2.0%v/wMEKP(8%ActiveOxygen) 25.00 OK Worldwide Exports

Test Particulars Observed Value Remarks Appearance Clear Pale Yellow OK Specific Gravity at 30°C 1.10 OK Acid Value, mgKOH/g 25.00 OK Volatile content, s by wt. 37.00 OK Viscosity at 30°C Brookfield Viscometer, Cps 240 OK Gel Time, minutes at 30°C 1.0% v/w Cobalt Octoate (3% Co) 2.0% w/w MEKP (8% Active Oxygen) 6Min OK Peak Exotherm Temprature, C 180 OK Worldwide Exports

Due to the relatively unstable nature of organic peroxides a loss of quality can be detected over a period of time. To minimize the loss of quality, we recommend a maximum storage temperature. (Ts max.) for each organic peroxide product. For MEKP (PX):Ts max.= 250C PHTHALATE FREE When stored under the recommended storage conditions, will remain within the limit for a period of at least six months after delivery. Worldwide Exports

General Name : Bp Paste Chemical Name : Benzoyl Peroxide Paste Peroxide Class : Diacyl Peroxide Structure : (C6H5CO2) 2 Molecular Weight : 242.2 Cas No. : 94-36-0 Packing : 50 Kg Wide Mouth Hdpe Drum Worldwide Exports

Cas No: 614-45-9 Formula : C6H5 -COOOC-(CH3)3 Molecular : Wt 194.2 Oxygen Content : 8.24 % Of Peroxide Other Name : Tert-butyl Perbenzoate, T-butyl Ester Peroxybezoic Peroxide Class : Peroxy Esters Intended Use : Initiator For Unsaturated Polyester Resin. Worldwide Exports

Due to the relatively unstable nature of organic peroxides a loss of quality can be detected over a period of time. To minimize the loss of quality, We recommend a maximum storage temperature (T, max.) for each organic peroxide product. For AMPEROX M60 T, max. = 25°C. When stored under the recommended storage conditions, AMPEROX M60 will remain within our specifications for a period of at least six months after delivery. Worldwide Exports

Due to the relatively unstable nature of organic peroxides a loss of quality can be detected over a period of time. To minimize the loss of quality, we recommend a maximum storage temperature (Ts max.) for each organic peroxide product. For MEKP Ts max.= 250C When stored under the recommended storage conditions, will remain within the limit for a period of at least three months after delivery. Worldwide Exports

Unlike glass fibers used for insulation, for the final structure to be strong, the fiber’s surfaces must be almost entirely free of defects, as this permits the fibers to reach gigapascal tensile strengths. If a bulk piece of glass were defect-free, it would be equally as strong as glass fibers; however, it is generally impractical to produce and maintain bulk material in a defect-free state outside of laboratory conditions. Worldwide Exports

Pigment pastes are produced by pasting or blending one or several pigments and/or fillers in a paste resin based on a polyester oligomer polyacrylate which is obtainable by radical polymerisation of. A) 80-50 wt % of. a) one or several hydroxyfunctional acrylic acid esters and/or methacrylic acid esters Worldwide Exports

Due to the relatively unstable nature of organic peroxides a loss of quality can be detected over a period of time. To minimize the loss of quality, we recommend a maximum storage temperature (Ts max.) for each organic peroxide product. For MEKP Ts max.= 250C When stored under the recommended storage conditions, will remain within the limit for a period of at least three months after delivery. Worldwide Exports

Miscible with organic solvents and oils. Suitable to use with other siccatives. Used for Polyester and Isocyanurate foam initiator. Potassium Octoate is used in conjunction with Cobalt for a synergistic effect and to reduce discoloration of the final Gel-Coat. Potassium may offer cost savings as well as a decline in gel-time drift. Worldwide Exports

In FRP Grade, Cobalt Octoate is combination of two metals. Combined % of two metal is active metal present in Cobalt Octoate. These compounds are promoters used in the curing of polyester and vinyl ester resins with methyl ethyl ketone peroxide (MEKP) type catalysts. Promoters are also called accelerators. They can be added to the resin by the supplier, in which case the resin is said to be pre-promoted. Alternatively, the manufacturer prior to adding catalyst to the resin ca

Combination driers of cobalt / zirconium/calcium or also cobalt / strontium / calcium are typically used in high solids, as are drier combinations. 5. As compared to lower solids alkyd paints, the level of through drier is higher, as in following example: 0.05% Cobalt. 0.4% Zirconium. Worldwide Exports

Nickel Octoate is a very toxic compound, it may cause cancer and damage fertility. It is harmful if inhaled or swallowed and may cause sensitization by skin contact. Nickel Octoate is very toxic to aquatic life with long lasting effects. Nickel Octoate is flammable. Worldwide Exports

Copper is an anti fouling agent. It is used in ship bottoms paints. Copper Octoate Hydrolyses gradually in to Copper Hydroxide & Octoic Acid in the presence of seawater, Copper Hydroxide is an active toxicant. It is used as a rot proofing agent in textiles, cordage etc. & to prevent dry rot & mildew growth in timber. Worldwide Exports

Iron Octoate is used in backing finishes, since it promotes rapid drying by polymerization. When used in air drying system it improves through drying. It is an excellent wetting agent for carbon black & iron oxide. It prevents adsorption of driers on the surface of the pigments & increases gloss. In air-dry finishes it is useful in eliminating film tackiness of paints containing a high percentage of non-drying oil component such as fish oil. It can be used as an adhesion prom

Cerium (Rare earth) is a primary drier, promotes polymerization and imparts through drying property. In alkyd based varnishes Cerium is more active as compared to lead. In contrast with lead driers, Cerium does not cause turbidity in oils and alkyd based varnishes. It has a synergistic effect when used in combination with Cobalt resulting in the need for using a lower percentage of Cobalt and thereby offering an economy. In air-drying white colourless or clear or pastel shade

Strontium Octoate is the replacement of Lead Octoate, where Lead free Paint/Ink is required. It improves through drying in adverse effect like high humidity & low temperatures. Strontium seems to overcome the insufficient Zirconium performance. Also unlike Zirconium, Strontium avoids yellowing. Strontium is also a good pigment wetting & dispersing agent preventing haze & wrinkling. Worldwide Exports

Calcium being an auxiliary drier, has little drying action in itself but is very useful in combination with active driers like Cobalt & Lead Octoate. In vehicles that show poor tolerance for lead, calcium can replace part of the lead with a larger amount of calcium to prevent the precipitation of the lead & maintain drying efficiency. Calcium is often used to replace lead where toxicity of lead must be avoided. Calcium is also useful as pigment wetting & dispersing agents & h

Zirconium is a most useful & efficient auxiliary drier. Zirconium like lead serves as a through drier & is generally used in combination with Cobalt, Manganese & Calcium. Unlike Lead, Zirconium is a poor pigment wetting & dispersing agent, hence combination with calcium is necessary. Zirconium is an active cross-linking agent & as such improves hardness of stoved films as well as their adhesions Zirconium is not as effective in phenolic resin based media it is recommended as

Zinc being an auxiliary drier, used in conjunction with redox metals. The primary function of zinc is to keep the film “Open” by retarding Surface dry, thus permitting hardening through out & preventing surface wrinkling, particularly in Cobalt containing films & enamels. Zinc is a powerful wetting & dispersing agent, & when incorporated early in formulation, it greatly reduces the time of mixing & grinding. Because of the extremely light colour, Zinc can be added without dis

Lead is a through drier & is always used as active or top drier. It promotes hard & through drying throughout the film & also increases flexibility, toughness & durability of the film. Lead drier can give rise to precipitation in the film as, Lead Octoate reacts with unreacted pthalic anhydride of alkyd resin, which could form Lead Pthalate, which may cause haziness & loss of gloss. In order to avoid this it is advisable to add Calcium Octoate first which acts as emulsifier &

Manganese driers are intermediate in activity & they have both oxidizing & polymerizing properties & hence can be used as surface & through drier. It is used alone in backing finishes & along with Cobalt & Lead in air drying applications. When used in combination with Lead, hard tough & durable films are produced. It is mainly used for exterior paints, floor finishes, backing enamels, foundry chemicals etc. Worldwide Exports

Cobalt Octoate is the most active surface drier. It promotes the polymerization of media, hardens the paint film, improves gloss and water resistance, and reduces brittleness. Careful use of Cobalt Octoate ensures a paint film with excellent gloss, free from frosting tendencies. Worldwide Exports